Poyerekeza ndi njerwa wamba za alumina, njerwa zathu zopepuka kwambiri za alumina zili ndi makhalidwe awa:
Kuchuluka kochepa kwa zinthu. Poyerekeza ndi njerwa wamba za alumina zokhala ndi 99% AI2O3 komanso kuchuluka kwa zinthu zosachepera 1.5 g/cm3, njerwa za alumina zopepuka kwambiri zimatha kuchepetsa kulemera kwa ng'anjo mokwanira kuti zisunge zinthu, mphamvu ndi ndalama;
Kukhazikika bwino kwa kutentha poyerekeza ndi njerwa wamba za alumina zokhala ndi kuchuluka kwa 1.5 g/cm3 ndi AI2O3≥99%;
Kutentha kotsika kwambiri, 30% yokha ya zinthu zachikhalidwe, Pa 400℃, kutentha kotsika kwa pamwamba pa njerwa ya alumina yachikhalidwe yokhala ndi kuchuluka kwa 1.5g/cm3 ndi AI2O3≥ 99% ndi 0.78w/(mK), pomwe kutentha kotsika kwa mbali yotentha ya ng'anjo ya Rongsheng's.
Njerwa ya alumina yopepuka kwambiri ndi 0.26w/(mK), ndipo mphamvu yake yotetezera kutentha ndi katatu kuposa yachikhalidwe. Kugwiritsa ntchito njerwa za alumina yopepuka kwambiri kungapangitse kutentha kochepa kumbali yozizira pansi pa kufunikira komweko kwa makulidwe a zigawo zotetezera kutentha ndi kukulirapo.
kusunga mphamvu, kapena wosanjikiza woonda kwambiri pansi pa zofunikira zomwezo za kutentha kwa mbali yozizira.
Itha kugwiritsidwa ntchito mwachindunji mu gawo logwirira ntchito la ng'anjo, ndipo imakana kwambiri kuwonongeka kwa hydrogen fluoride mu ng'anjo ya anode.
Kukula kwake kuli mkati mwa 0.05mm, miyeso yake ikhoza kusinthidwa malinga ndi zosowa za makasitomala.
Kufotokozera
| Chinthu | RS-KXQ1 |
| BD,(g/cm3) | ≤0.85 |
| CCS,(MPa) | ≥3 |
| TC,400℃(W/m ·K) | ≤0.26 |
| PLC (1500℃ * 6),% | ≤1.0 |
| Al2O3, % | ≥99％ |